| 1Cr13AI4 | oCr21A15 | oCr21A16 | oCr21A14 | oCr21A16Nb | oCr27A17Mo2 | ||
| 主要化學成份 Main chemical Composition | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
| AI | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 | |
| Re | 適量 opportune amount | 適量 opportune amount | 適量 opportune amount | 適量 opportune amount | 適量 opportune amount | 適量 opportune amount | |
| Fe | 餘量 Rest | 餘量 Rest | 餘量 Rest | 餘量 Rest | 餘量 Rest | 餘量 Rest | |
| ? | ? | ? | ? | ? | Nb0.5 | Mo1.8-2.2 | |
| 元件最高使用溫度(℃) Max.continuous service temp.of element(℃) | 950 | 1250 | 1250 | 1100 | 1350 | 1400 | |
| 電阻率20℃(μΩ·m) Resistivity at 20℃ | 1.25 | 1.42 | 1.42 | 1.23 | 1.43 | 1.53 | |
| 密度 Density(g/cm3) | 7.40 | 7.10 | 7.16 | 7.35 | 7.10 | 7.10 | |
| 導熱系數 (KJ/m.h.℃) Thermal conductivity | 52.7 | 46.1 | 63.2 | 46.9 | 46.1 | 45.2 | |
| 線脹系數 Coefficient of lineas expansion(α*10-6/℃) | 15.4 | 16.0 | 14.7 | 13.5 | 16.0 | 16.0 | |
| 熔點約值 Melting point(approx.)(℃) | 1450 | 1500 | 1500 | 1500 | 1510 | 1520 | |
| 抗張強度Tensile strength(kg/mm2) | 60-70 | 65-80 | 65-80 | 65-80 | 65-80 | 70-85 | |
| 延伸率% Elongation at ruptrue | >16 | >12 | >12 | >12 | >12 | >10 | |
| 斷麵收縮率% Variation of area | 65-75 | 60-75 | 65-75 | 65-75 | 65-75 | 65-75 | |
| 反復彎曲數(F/R) Repeat bending frequency | >5 | >5 | >5 | >5 | >5 | >5 | |
| 硬度 Hardness(H.B.) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | |
| 顯微組織 Micrographic structure | 鐵素體 Ferrite | 鐵素體 Ferrite | 鐵素體 Ferrite | 鐵素體 Ferrite | 鐵素體 Ferrite | 鐵素體 Ferrite | |
| 磁性 Magnetic properties | 磁性Magnetic | 磁性Magnetic | 磁性Magnetic | 磁性Magnetic | 磁性Magnetic | 磁性Magnetic | |