化學成份
單位:(%)碳 C :2.00~2.30矽 Si:≤0.40錳 Mn:≤0.40硫 S :≤0.030磷 P :≤0.030鉻 Cr:11.50~13.00鎳 Ni:允許殘餘含量≤0.25銅 Cu:允許殘餘含量≤0.30鈷 Co:≤1.00力學性能
硬度 :退火,269~217HB,壓痕直徑3.7~4.1mm;淬火,≥58HRC熱處理
金相組織:回火馬氏體+未溶碳化物+殘餘奧氏體。交貨狀態:鋼材以退火狀態交貨。淬火溫度
Cr12淬火950~1000℃油淬,二次回火550℃高溫淬火1100-1150℃,低溫淬火960-1050℃,回火550-650℃,前者有二次硬化現象,回火不少於2次,每次2h,回火後可空冷或油冷,高溫淬火前最好進行2次預熱,在高溫加熱時,需采取保護措施,以防氧化。