| Bayblend ET1100 | (PC+ABS) blend; 10 % mineral filled; extrusion grade; very high heat resistance; Vicat/B 120 = 142 °C; reduced coefficient of thermal dilatation; tensile modulus = 3300 MPa. |     | |
 | Bayblend ET3032 FR | Rubber modified PC blend; 10 % mineral filled; flame-retardant; extrusion grade; Vicat/B 120 temperature = 108 °C; good extrusion and vacuum-forming behaviour; UL 94 V-0 (0.75 mm) (Bayer internal test); halogen-free according to DIN VDE 0472,815; glow wire temperature (GWFI): 960 °C at 2.0 mm. | |
| Bayblend FR3000 | (PC+ABS) blend; unreinforced; flame-retardant; injection molding grade; easy-flow grade; Vicat/B 120 temperature = 97 °C; UL recognition 94 V-0 (1.5 mm); antimony-, chlorine- and bromine-free flame retardant; glow wire test (GWFI): 960 °C (2.0 mm); no juicing; good light stability. | |
| Bayblend FR3000 HI | (PC+ABS) blend; unreinforced; flame-retardant; injection molding grade; general purpose; compared to FR3000 improved chemical resistance and stress cracking behavior; Vicat/B 120 temperature = 97 °C; UL recognition 94 V-0 at 1.5 mm. | |
| Bayblend FR3002 | (PC+ABS) blend; unreinforced; flame-retardant; injection molding grade; Vicat/B 120 temperature = 99 °C; UL recognition 94 V-0 (1.0 mm); antimony- chlorine- and bromine-free flame retardant; glow wire test (GWFI): 960 °C (2.0 mm); for notebooks and thinwall applications. | | |
| Bayblend FR3005 | (PC+ABS) blend; unreinforced; flame-retardant; injection molding grade; easy-flow grade; Vicat/B 120 temperature = 95 °C; UL recognition 94 V-0 (1.5 mm); antimony-, chlorine- and bromine-free flame retardant; glow wire test (GWFI): 960 °C (2.0 mm); good light stability. | |
| Bayblend FR3005 HF | (PC+ABS) blend; unreinforced; flame-retardant; injection molding grade; very easy-flow grade; Vicat/B 120 temperature = 96 °C; UL recognition 94 V-0 (1.5 mm); antimony-, chlorine- and bromine-free flame retardant. | |
| Bayblend FR3006 | (PC+ABS) blend; unreinforced; flame-retardant; injection molding grade; high heat resistance; Vicat/B 120 = 110 °C; easy flow; UL recognition 94 V-1 at 1.5 mm and V-0 at 2.0 mm; antimony-, chlorine- and bromine-free flame retardant. | |
| Bayblend FR3008 | (PC+ABS) blend; unreinforced; flame-retardant; injection molding grade; improved chemical and hydrolysis resistance; HDT/A >= 85 °C; Vicat/B 120 temperature = 103 °C; UL recognition 94 V-0 (1.5 mm); antimony-, chlorine- and bromine-free flame retardant; glow wire test (GWFI): 960 °C (2.0 mm); good light stability. | |
| Bayblend FR3008 HR | (PC+ABS) blend; unreinforced; flame-retardant; injection molding grade; improved chemical and very good hydrolysis resistance; HDT/A >= 85 °C; Vicat/B 120 temperature = 103 °C; UL recognition 94 V-0 (1.5 mm); antimony-, chlorine- and bromine-free flame retardant; glow wire test (GWFI): 960 °C (2.0 mm); good light stability. | |
| Bayblend FR3010 | (PC+ABS) blend; unreinforced; flame-retardant; injection molding grade; increased heat resistance; Vicat/B 120 temperature = 110 °C; UL recognition 94 V-0 (1.5 mm); antimony-, chlorine- and bromine-free flame retardant; glow wire test (GWFI): 960 °C (2.0 mm); improved chemical resistance and stress cracking behavior; successor to FR2010. | |
| Bayblend FR3010 IF | (PC+ABS) blend; unreinforced; flame-retardant; injection molding grade; increased heat resistance; Vicat/B 120 temperature = 108 °C; improved flammability; UL recognition 94 5VB (1.5 mm); antimony-, chlorine- and bromine-free flame retardant; glow wire test (GWFI): 960 °C (2.0 mm); improved flow compared to FR3010. | |
| Bayblend FR3011 | (PC+ABS) blend; unreinforced; flame-retardant; injection molding grade; good flow; high heat resistance; Vicat/B 120 temperature = 118 °C; UL recognition 94 V-0 (1.5 mm); antimony-, chlorine- and bromine-free flame retardant; glow wire test (GWFI): 960 °C (2.0 mm); good light stability. | |
| Bayblend FR3020 | (PC+ABS) blend; 5 % mineral filled; flame retardant; for thin-wall applications; injection molding; Vicat/B 120 = 103 °C; HDT/A >= 85 °C; very good UL recognition in small wall thicknesses (V-0 at 0.75 mm); antimony-, chlorine- and bromine-free flame retardant. | |
| Bayblend FR3021 | (PC+ABS) blend; 15 % mineral filled; flame retardant; injection molding grade; increased stiffness; tensile modulus = 4800 MPa; Vicat/B 120 temperature = 98 °C; UL recognition 94 V-0 (1.5 mm); antimony-, chlorine- and bromine-free flame retardant; glow wire test (GWFI): 960 °C (2.0 mm). | |
| Bayblend FR3030 | (PC+ABS) blend; unreinforced; flame-retardant; extrusion grade; Vicat/B 120 temperature = 115 °C; good extrusion and vacuum-forming behaviour; UL recognition 94 V-0 (1.5 mm); halogen-free according to DIN VDE 0472,815; glow wire temperature (GWFI): 960 °C at 1.0 mm. | |
| Bayblend FR3100 TV | (PC+ABS) blend; unreinforced; flame-retardant; injection molding grade; high heat resistance; Vicat/B 120 = 110 °C; improved impact strength and chemical resistance; UL recognition 94 V-1 at 1.5 mm and V-0 at 2.0 mm; antimony-, chlorine- and bromine-free flame retardant. | |
| Bayblend FR3110 TV | (PC+ABS) blend; unreinforced; flame-retardant; injection molding grade; high heat resistance; Vicat/B 120 = 110 °C; easy flow; UL recognition 94 V-0 at 1.5 mm (Bayer internal test); antimony-, chlorine- and bromine-free flame retardant. |