原料技術數據| 性能項目 | 試驗條件[狀態] | 測試方法 | 測試數據 | 數據單位 |
| 物理性能 | 比重 | 固體 | ASTM D 792 | 1.20 | --- |
| 比容 | --- | ASTM D 792 | 23.10 | in3/lb |
| 模塑收縮量 | flow,0.125" | | xflow,0.125" |
| --- | | | |
| 機械性能 | 撓曲模量 | 0.125" | ASTM D 790 | 285000 | psi |
| 抗拉強度 | 屈服,類型I,0.125" | ASTM D 638 | 7900 | psi |
| 拉伸伸長 | 斷裂,類型I,0.125" | ASTM D 638 | 150.0 | % |
| 撓曲強度 | 屈服,0.125" | ASTM D 790 | 11900 | psi |
| 加工性能 | 排氣槽深度 | --- | --- | 0.0005-0.0008 | in |
| 溫度 | 熔體溫度 | | 註嘴溫度 | | 前段溫度 | | 中段溫度 | | 後段溫度 | | 模具溫度 |
| --- | --- | | 500-530 | | 490-520 | | 490-530 | | 480-520 | | 470-510 | | 150-190 |
| | deg F | | deg F | | deg F | | deg F | | deg F | | deg F |
|
| 乾燥溫度 | --- | --- | 230 | deg F |
| --- | --- | | |
| 含濕量（最大） | --- | --- | 0.02 | % |
| 背壓 | --- | --- | 50-100 | psi |
| 螺桿速度 | --- | --- | 50-80 | rpm |
| 推薦註射量 | --- | --- | 50-80 | % |
| 合模力噸數 | --- | --- | 3-6 | tons/psi |
| 熱 性 能 | | HDT(熱畸變溫度) | 66 psi,0.250",未退火 | | 264 psi,0.250",未退火 |
| --- | | | |
| 其它性能 | | 伊佐德沖擊值 | 缺口,73F | | 缺口,32F | | 缺口,-22F |
| --- | | ASTM D 256 | | ASTM D 256 | | ASTM D 256 |
| | |