| 性能項目試驗條件[狀態]測試方法測試數據數據單位 |
| 基本性能平衡吸水率23℃，相對濕度50%ASTM D-5700.32% |
| 熔體流動速率300℃/1.2kgASTM D-123810g/10min |
| 吸水率24hr,23℃ASTM D-5700.15% |
| 物理性能阻燃等級1.6mmUL 94HB |
| 透光率ASTM D-100389% |
| 折射率ASTM D-5421.586 |
| 模具收縮率ASTM D-9550.005-0.007in/in |
| 阻燃等級3.2mmUL 94HB |
| 比重ASTM D-7921200kg/m3 |
| 霧度ASTM D-10030.7-1.5% |
| 機械性能拉伸模量ASTM D-6382410MPa |
| 落錘沖擊強度總能量@23℃ASTM D-376387J |
| 沖擊強度23℃ASTM D-256未破裂 |
| 彎曲強度ASTM D-79096MPa |
| 拉伸強度屈服點50mm/minASTM D-63860MPa |
| 斷裂點-ASTM D-63871MPa |
| 洛氏硬度ASTM D-785118R標度 |
| 洛氏硬度ASTM D-78573M標度 |
| 缺口沖擊強度23℃ASTM D-256900j/m |
| 伸長率屈服點ASTM D-6386% |
| 斷裂點ASTM D-638150% |
| 彎曲模量ASTM D-7902410MPa |
| 電氣性能介電強度60HzASTM D-14917V/mil |
| 輝光燈絲測試2mm，5sIEC 695-2-1850℃ |
| 體積電阻23℃，乾ASTM D-2572.0×1017Ω.cm |
| 損耗因素60HzASTM D-1500.001 |
| 球狀壓痕溫度IEC 598-1>125℃ |
| 對比電弧徑跡指數2mmIEC 112250V |
| 熱性能熱變形溫度未退火@1.82MPaASTM D-648128℃ |
| 熱變形溫度退火@1.82MPaASTM D-648141℃ |
| 平均燃燒系數ASTM D-63525mm |
| 維卡軟化點50℃/小時，50n重ASTM D-1525149℃ |
| 線性熱收縮率-40℃～82℃ASTM D-69668×10-6mm/mm/℃ |
| 熱變形溫度退火@0.45MPaASTM D-648144℃ |
| 其它性能需氧系數ASTM D-286326% |