產品參數
| 性能項目 | 試驗條件[狀態] | 測試方法 | 測試數據 | 數據單位 | |
| 物理性能 | 熔體流動速率 | 200℃ 5kg | ASTM D-1238 | 5.2 | g/10min |
| 熔體流動速率 | 220℃×10kg | ASTM D-1238 | 60 | g/10min | |
| 比重 | ASTM D-792 | 1.20 | 23/23℃ | ||
| 機械性能 | 彎曲彈性率 | ASTM D-790 | 3.0×105 | lb/in2 | |
| IZOD沖擊強度 | 1/4〃 | ASTM D-256 | 16 | kg.cm/cm | |
| 伸長率 | ASTM D-638 | 15 | % | ||
| 引張強度 | ASTM D-638 | 390 | kg/cm2 | ||
| 彎曲強度 | ASTM D-790 | 620 | kg/cm2 | ||
| 彎曲強度 | ASTM D-790 | 8800 | lb/in2 | ||
| IZOD沖擊強度 | 1/8" | ASTM D-256 | 3.7 | ft.lb/in | |
| 引張強度 | ASTM D-638 | 5530 | lb/in2 | ||
| 洛氏硬度 | ASTM D-785 | 100 | R | ||
| IZOD沖擊強度 | 1/4〃 | ASTM D-256 | 2.9 | ft.lb/in | |
| 彎曲彈性率 | ASTM D-790 | 2.1×104 | kg/cm2 | ||
| IZOD沖擊強度 | 1/8" | ASTM D-256 | 20 | kg.cm/cm | |
| 熱性能 | 燃燒性 | File No. E56070 UL&C-UL | 1/16"V-O，1/10"5VA | ||
| 熱變形溫度 | ASTM D-648 | 83(181) | ℃ | ||
| 維卡軟化點 | ASTM D-1525 | 194 | ℉ | ||
| 維卡軟化點 | ASTM D-1525 | 90 | ℃ | ||
| 熱變形溫度 | ASTM D-648 | 73(165) | ℉ | ||
POLYLAC® PA-765
丙烯腈丁二烯苯乙烯
CHI MEI CORPORATION
產品說明:
POLYLAC® PA-765是一種丙烯腈丁二烯苯乙烯(ABS)產品,。 它可以通過註射成型進行加工,在北美洲、非洲和中東、拉丁美洲、歐洲或亞太地區有供貨。
特性包括:
特性包括:
- 阻燃/額定火焰
- 通過 ROHS 認證
| 物理性能 | 額定值 | 單位製 | 測試方法 |
比重 | |||
-- | 1.19 | ASTM D792 | |
-- | 1.19 | g/cm³ | ISO 1183 |
熔流率（熔體流動速率） | ASTM D1238 | ||
200°C/5.0 kg | 5.0 | g/10 min | |
220°C/10.0 kg | 56 | g/10 min | |
溶化體積流率（MVR） (220°C/10.0 kg) | 2.99 | in³/10min | ISO 1133 |
| 硬度 | 額定值 | 單位製 | 測試方法 |
洛氏硬度 (R 級) | 100 | ASTM D785 | |
球壓硬度 (H 358/30) | 11500 | psi | ISO 2039-1 |
| 機械性能 | 額定值 | 單位製 | 測試方法 |
拉伸應力 | |||
屈服 | 5660 | psi | ISO 527-2/50 |
斷裂 | 4930 | psi | ISO 527-2/50 |
0.118 in 3 | 5550 | psi | ASTM D638 |
伸長率 | |||
斷裂, 0.118 in 3 | 15 | % | ASTM D638 |
斷裂 | 10 | % | ISO 527-2/50 |
彎曲模量 | |||
0.236 in 4 | 299000 | psi | ASTM D790 |
-- 5 | 261000 | psi | ISO 178 |
彎曲強度 | |||
0.236 in 4 | 8820 | psi | ASTM D790 |
-- 5 | 7980 | psi | ISO 178 |
| 沖擊性能 | 額定值 | 單位製 | 測試方法 |
簡支梁缺口沖擊強度 | 9.5 | ft·lb/in² | ISO 179 |
懸壁梁缺口沖擊強度 | |||
73°F, 0.118 in | 4.0 | ft·lb/in | ASTM D256 |
73°F, 0.236 in | 3.3 | ft·lb/in | ASTM D256 |
-- | 8.1 | ft·lb/in² | ISO 180/1A |
| 熱性能 | 額定值 | 單位製 | 測試方法 |
載荷下熱變形溫度 | |||
264 psi, 未退火 | 163 | °F | ASTM D648 |
264 psi, 未退火 | 165 | °F | ISO 75-2/A |
264 psi, 退火 | 181 | °F | ASTM D648 |
264 psi, 退火 | 194 | °F | ISO 75-2/A |
維卡軟化溫度 | |||
-- | 194 | °F | ASTM D1525 6, ISO 306/A50 6 |
-- | 172 | °F | ISO 306/B50 |
| 可燃性 | 額定值 | 測試方法 | |
UL 阻燃等級 | UL 94 | ||
0.0394 in | V-1 | ||
0.0591 in | V-0 | ||
0.0630 in | V-0 | ||
0.0984 in | 5VA |
顯示器、機頂盒、調製解調器、電源關開麵板、電源插座、汽車電池、收款機外殼、電表殼體、打印機外殼、搖控器、燈箱、傳真機、投影機、大型事務機、打印機、咖啡機、電視前後框、DVD撥放器、汽車音響控製麵板
乾燥溫度 | 176 到 185 | °F | |
乾燥時間 | 2.0 到 4.0 | hr | |
料筒後部溫度 | 356 到 410 | °F | |
料筒中部溫度 | 374 到 428 | °F | |
料筒前部溫度 | 374 到 428 | °F | |
模具溫度 | 104 到 158 | °F | |
註塑壓力 | 711 到 1140 | psi | |
註射速度 | 慢到中等 | ||
保壓 | 284 到 711 | psi | |
背壓 | 71.1 到 142 | psi | |
墊層 | 0.125 | in |