產品參數
| 性能項目 | 試驗條件[狀態] | 測試方法 | 測試數據 | 數據單位 | ||
| 基本性能 | 熔體流動速率 | ASTM D-1238 | 2.0 | g/10min | ||
| 密度 | ASTM D-1505 | 0.920 | g/cm3 | |||
| 機械性能 | 落球沖擊強度 | ASTM D-1709 | 120 | g | ||
| 抗撕裂性 | MD | ASTM D-1922 | 40 | g/25μm | ||
| TD | ASTM D-1922 | 430 | g/25μm | |||
| 拉力斷裂強度 | MD | ASTM D-882B | 360 | Kg/cm2 | ||
| TD | ASTM D-882B | 280 | Kg/cm2 | |||
| 拉力降伏強度 | MD | ASTM D-882B | 100 | Kg/cm2 | ||
| TD | ASTM D-882B | 110 | Kg/cm2 | |||
| 1%伸長彈性系數 | MD | ASTM D-882B | 1500 | Kg/cm2 | ||
| TD | ASTM D-882B | 2100 | Kg/cm2 | |||
| 拉力斷裂伸長率 | MD | ASTM D-882B | 600 | % | ||
| TD | ASTM D-882B | 800 | % | |||
| 熱性能 | 脆化溫度 | ASTM D-746 | <-70 | ℃ | ||
| 熔點 | DSC | 122 | ℃ | |||
| 軟化點 | ASTM D-1525 | 93 | ℃ | |||
| 其它性能 | 開口劑 | 中 | ||||
| 滑劑 | 中 | |||||
| 濁度 | ASTM D-1003 | 22 | % | |||
| 透明度 | 60 | % | ||||
| 光澤度 | 45℃ | ASTM D-2457 | 52 | % | ||
聚丙烯為無毒、無臭、無味的乳白色高結晶的聚合物，密度隻有0. 90--"0. 91g/cm3，是目前所有塑料中最輕的品種之一。它對水特別穩定，在水中的吸水率僅為0. 01%，分子量約8萬一15萬。成型性好，但因收縮率大(為1%~2.5%）.厚壁製品易凹陷，對一些尺寸精度較高零件，很難於達到要求，製品表麵光澤好。
規格級別外觀顏色該料用途備註說明
| 高抗沖,高流動 其它 嵌段共聚註塑 | ||
| 大型容器 | ||
| 特性：抗沖擊強度、高流動性、高強性，嵌段共聚 | ||
③原料技術數據
| 性能項目 | 試驗條件[狀態] | 測試方法 | 測試數據 | 數據單位 | |
| 基本性能 | 熔體流動速率 | ASTM D-1238 | 25 | g/10min | |
| 物理性能 | 收縮率 | SK | 1.5-2.0 | % | |
| 機械性能 | IZOD沖擊強度 | -20℃ | ASTM D-256 | 3 | kg.cm/cm |
| 洛氏硬度 | ASTM D-785 | 95 | R Scale | ||
| IZOD沖擊強度 | 23℃ | ASTM D-256 | 8 | kg.cm/cm | |
| 斷裂伸長率 | ASTM D-638 | >300 | % | ||
| 彎曲彈性系數 | ASTM D-790 | 16000 | kg/cm2 | ||
| 拉伸斷裂強度 | ASTM D-638 | 290 | kg/cm2 | ||
| 熱性能 | 加速老化時間 | ASTM D-3012 | 360 | hr | |
| 熱變形溫度 | ASTM D-648 | 110 | ℃ | ||
| 維卡軟化點 | ASTM D-1525 | 150 | ℃ | ||
| 其它性能 | 流動性 | SK | >800 | mm | |