Property

T Block

Requirements for ISO 
13356:1997

Chemical compositions:

ZrO2+HfO2+Y2O3

ZrO2

Y2O3

Al2O3

Other oxide

99.6wt%

94.6

5.0wt%

0.25wt%

<0.15t%

>99.0wt%

4.5 to 5.4 wt%

<0.5wt%

<0.5wt%

Bending strength

1150MPa

≥500MPa

Sintering density

6.055 ~6.065g/cm3

≥6.0 g/cm3

Young's modulus

200GPa

Average grain size

0.52+/-0.05µm

≤0.6µm(ISO 13356)

Fracture Toughness

9 Mpa.m1/2

Thermal conductivity

3.0 W / mK

Coefficient of thermal expansion( 20 - 400°C)

9.6 *10-6 / K

chemical solubility

10µg/cm2

100µg/cm2(ISO 6872)

Radioactivity

0.005Bq/g 

1.0 Bq/g（ISO 6872）