船板力學性能與化學成分
船板力學性能與化學成分
一般強度船體結構鋼力學性能與化學成份
鋼材級別 | 屈服點 σs(MPa)不小於 | 抗拉強度 σb(MPa) | 伸長率σ% 不小於 | 碳 C | 錳 Mn | 矽 Si | 硫 S | 磷 P |
A | 235 | 400-520 | 22 | ≤0.21 | ≥2.5 | ≤0.5 | ≤0.035 | ≤0.035 |
B | ≤0.21 | ≥0.80 | ≤0.35 |
|
|
|
|
|
D | ≤0.21 | ≥0.60 | ≤0.35 |
|
|
|
|
|
E | ≤0.18 | ≥0.70 | ≤0.35 |
|
|
|
|
|
高強度船體結構鋼力學性能與化學成份
鋼材級別 | 屈服點σs (MPa)不小於 | 抗拉強度 σb(MPa) | 伸長率σ% 不小於 | 碳 C | 錳 Mn | 矽 Si | 硫 S | 磷 P |
A32 | 315 | 440-570 | 22 | ≤0.18 | ≥0.9-1.60 | ≤0.50 | ≤0.035 | ≤0.035 |
D32 |
|
|
|
|
|
|
|
|
E32 |
|
|
|
|
|
|
|
|
F32 | ≤0.16 | ≤0.025 | ≤0.025 |
|
|
|
|
|
A36 | 355 | 490-630 | 21 | ≤0.18 | ≤0.035 | ≤0.035 |
|
|
D36 |
|
|
|
|
|
|
|
|
E36 |
|
|
|
|
|
|
|
|
F36 | ≤0.16 | ≤0.025 | ≤0.025 |
|
|
|
|
|
A40 | 390 | 510-660 | 20 | ≤0.18 | ≤0.035 | ≤0.035 |
|
|
D40 |
|
|
|
|
|
|
|
|
E40 |
|
|
|
|
|
|
|
|
F40 | ≤0.16 | ≤0.025 | ≤0.025 |
|