| 原產地：宜春 | 種類：鋰長石 | 礦床類型：巖漿巖型 |
| K2O含量＞：3.1（%） | Fe2O3含量＜：0.04（%） | Na2O含量：6.3（%） |
| Al2O3含量：17.48（%） | SiO2含量：71.23（%） | 密度：2.8（g/cm3） |
| 莫氏硬度：6.5 | 熔點：1150（℃） | 顏色：白色 |
| 水分：≤18 | 白度：70 | 鋰：0.8-1.4 |
ng>廠傢供應優質鋰長石ng>
本產品具有純度高儲量大品位穩定性好,可大量供貨.產品分破碎石米,雷蒙粉.水磨三種方式,可大量用於陶瓷釉料,熔塊等產品.包裝50kg每袋.
ng>鋰長石粉－－富含鋰、鉀、鈉、銣、銫等元素，ng>
ng>白度好，含鐵等雜質低、粒度均勻，是玻璃、陶瓷生產的優質原料。ng>
ng>鋰長石質量指標表ng>
ng>元素ng> | ng>Li2Ong> | ng>K2Ong> | ng>Na2Ong> | ng>Al2O3ng> | ng>Si2ong> | ng>Fe O2ng> | ng>Rb2Ong> | ng>Cs2Ong> |
ng>含量（%)ng> | ng>0.8-1.0ng> | ng>1.7-2.2ng> | ng>4.5-4.7ng> | ng>18-22.0ng> | ng>67-71ng> | ng>≤0.10ng> | ng>0.3±ng> | ng>0.058±ng> |
| ng>粒度mmng> | ng>0.2ng> | ng>0.105ng> | ng>0.073ng> | ng>0.038ng> | ng>—0.038ng> | ng>合計ng> |
| ng>產率%ng> | ng>37.16ng> | ng>13.75ng> | ng>25.15ng> | ng>13.35ng> | ng>11.59ng> | ng>100ng> |
ng> ng>
ng>鋰長石粉篩析情況表ng>
| ng>粗長石ng> | ng>篩孔（mm)ng> | ng>>0.9ng> | ng>0.9~0.5ng> | ng>0.5~0.2ng> | ng>0.2~0.105ng> | ng>0.105~0.074ng> | ng><0.074ng> | ng>合計ng> |
| ng> ng> | ng>含量ng> | ng>0ng> | ng>3.678ng> | ng>28.962ng> | ng>37.115ng> | ng>16.638ng> | ng>13.58 ng> | ng>100ng> |
| ng>細長石ng> | ng>篩孔（mm）ng> | ng>>0.074ng> | ng>0.074~0.038ng> | ng>0.038~0.2ng> | ng><0.02ng> | ng> ng> | ng> ng> | ng>合計ng> |
| ng> ng> | ng>含量ng> | ng>6.27ng> | ng>35.38ng> | ng>48.15ng> | ng>10.55ng> | ng> ng> | ng> ng> | ng>100 ng> |
歡迎來電咨詢，價格麵議！！
ng>一、產品特性ng>
ng>1、白度好，成分穩定，性價比高ng>
ng>2、高鋁低鐵低鈦，性能穩定ng>
ng>3、強烈的助熔效果，降低玻璃的熔點溫度ng>
ng>4、減少氧化鋁，純堿的用量ng>
二、鋰長石代替鉀長石生產平板玻璃的使用效果
1、代替鉀長石，玻璃成份無需作較大的調整，對玻璃的熔化，成型不會造成不良反應。
2、能加熔化速度，提高玻璃液的均勻性，具有明顯的明熔效果。
3、鋰長石用於平板玻璃生產，按350噸窯的使用情況計算，玻璃中引入0.12%的Li2O每年可節約純堿262.8噸。再者鋰長石價格低於鉀長石，並且本身無需粉碎，降低瞭玻璃成本。
4、鋰長石中含鐵量比鉀長石低3倍以上，能降低玻璃中的Fe2O3含量，玻璃的透光性能明顯改善，對於浮法工藝生產厚玻璃十分有利。
5、鋰長石成份穩定性好於鉀長石，生產好控制，玻璃密度波動范圍小。